Quality Supplier TANKII alloy Nicr3020 Sheet for Resistive Elemen For Electric Element
(It is a nickel-chromium heating conductor alloy for operating temperatures of up to 1150 °C and often contains additives of rare earths for a higher resistance to oxidation, especially with frequent switching operations or broad temperature variations.
The resistance to atmospheric corrosion at 20 °C is high up to the upper operating temperature the resistance to air and other oxygen-containing gases as well as to nitrogen-containing low-oxygen gases is high as well, yet it is low to oxidizing as well as reducing gases containing sulphur.
The resistance to carbonizing is high. Application for industrial electric furnaces, enamelling furnaces, household appliances, night-current storage space-heaters.
Normal composition%
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | Other |
| Max | |||||||||
| 0.08 | 0.02 | 0.015 | 1.00 | 1.0~2.0 | 18.0~21.0 | 30.0~34.0 | - | Bal. | - |
Typical Mechanical properties(1.0mm)
| Yield strength | Tensile Strength | Elongation |
| Mpa | Mpa | % |
| 340 | 675 | 35 |
Typical Physical properties
| Density (g/cm3) | 7.9 |
| Electrical resistivity at 20ºC(Om*mm2/m) | 1.04 |
| Conductivity coefficient at 20ºC (WmK) | 13 |
| Coefficient of thermal expansion | |
| Temperature | Coefficient of Thermal Expansion x10-6/ºC |
| 20 ºC- 1000ºC | 19 |
| Specific heat capacity | |
| Temperature | 20ºC |
| J/gK | 0.50 |
| Melting point (ºC) | 1390 |
| Max continuous operating temperature in air (ºC) | 1100 |
| Magnetic properties | non-magnetic |
Temperature Factors Of Electrical Resistivity
| 20ºC | 100ºC | 200ºC | 300ºC | 400ºC | 500ºC | 600ºC |
| 1 | 1.023 | 1.052 | 1.079 | 1.103 | 1.125 | 1.141 |
| 700ºC | 800ºC | 900ºC | 1000ºC | 1100ºC | 1200ºC | 1300ºC |
| 1.158 | 1.173 | 1.187 | 1.201 | 1.214 | 1.226 | - |
| Chemical Composition and Propertes: | ||||||
| Propertes/Grade | NiCr 80/20 | NiCr 70/30 | NiCr 60/15 | NiCr 35/20 | NiCr 30/20 | |
| Main Chemical Composition(%) | Ni | Bal. | Bal. | 55.0-61.0 | 34.0-37.0 | 30.0-34.0 |
| Cr | 20.0-23.0 | 28.0-31.0 | 15.0-18.0 | 18.0-21.0 | 18.0-21.0 | |
| Fe | ≤ 1.0 | ≤ 1.0 | Bal. | Bal. | Bal. | |
| Max Working Temperature(ºC) | 1200 | 1250 | 1150 | 1100 | 1100 | |
| Resistivity at 20ºC (μ Ω · m) | 1.09 | 1.18 | 1.12 | 1.04 | 1.04 | |
| Density(g/cm3) | 8.4 | 8.1 | 8.2 | 7.9 | 7.9 | |
| Thermal Conductivity (KJ/m· h· ºC) | 60.3 | 45.2 | 45.2 | 43.8 | 43.8 | |
| Coefficient of Thermal Expansion (α × 10-6/ºC) | 18 | 17 | 17 | 19 | 19 | |
| Melting PointºC) | 1400 | 1380 | 1390 | 1390 | 1390 | |
| Elongation(%) | > 20 | > 20 | > 20 | > 20 | > 20 | |
| Micrographic Structure | austenite | austenite | austenite | austenite | austenite | |
| Magnetic Property | nonmagnetic | nonmagnetic | nonmagnetic | nonmagnetic | nonmagnetic | |
| Chemical Composition | Nickel 30%, Chrome 20% |
| Condition | Bright/Acid white/Oxidied Color |