0cr25al5 CrFeAl 145 Hot Rolled Round Bar Round Material Alloy Steel Bar Bright Annealing
|
Grade
|
0Cr25Al5
|
|
Size
|
10-60mm
|
|
Surface
|
oxidized
|
|
Resistivity
|
1.42±0.07μΩ.m
|
|
Highest temperature
|
1250ºC
|
|
Density
|
7.1g/cm³
|
|
Tensile strength
|
750N/mm²
|
|
Elongation
|
≥12%
|
|
Grade
|
Highest temperature
|
Resistivity
|
Melting point
|
Tensile strength
|
Elongation
|
|
0Cr21Al4
|
1100ºC
|
1.23±0.06μΩ.m
|
1500ºC
|
750
|
≥12
|
|
0Cr25Al5
|
1250ºC
|
1.42±0.07μΩ.m
|
1500ºC
|
750
|
≥12
|
|
0Cr21Al6NbCo
|
1350ºC
|
1.43±0.07μΩ.m
|
1510ºC
|
750
|
≥12
|
|
0Cr27Al7Mo2
|
1400ºC
|
1.53±0.07μΩ.m
|
1520ºC
|
750
|
≥10
|
|
KSC
|
1350ºC
|
1.44±0.05μΩ.m
|
1510ºC
|
750
|
≥16
|
|
Cr20Ni80
|
1200ºC
|
1.09±0.05μΩ.m
|
1400ºC
|
750
|
≥20
|
|
Cr15Ni60
|
1150ºC
|
1.12±0.05μΩ.m
|
1390ºC
|
750
|
≥20
|
|
Cr20Ni35
|
1100ºC
|
1.04±0.05μΩ.m
|
1390ºC
|
750
|
≥20
|
|
Cr20Ni30
|
1100ºC
|
1.04±0.05μΩ.m
|
1390ºC
|
750
|
≥20
|
|
Grade
|
Chemical composition%
|
||||||||
|
C
|
P
|
S
|
Mn
|
Si
|
Cr
|
Ni
|
Al
|
Fe
|
|
|
≤
|
|||||||||
|
0Cr21Al4
|
0.12
|
0.025
|
0.025
|
0.7
|
≤1.0
|
17-21
|
≤0.6
|
3-4
|
balance
|
|
0Cr25Al5
|
0.06
|
0.025
|
0.02
|
0.5
|
≤0.6
|
23-26
|
≤0.6
|
4.5-6.5
|
balance
|
|
0Cr21Al6Nb
|
0.05
|
0.025
|
0.02
|
0.5
|
≤0.6
|
21-23
|
≤0.6
|
5-7
|
balance
|
|
0Cr27Al7Mo2
|
0.05
|
0.025
|
0.02
|
0.2
|
≤0.4
|
26.5-27.8
|
≤0.6
|
6-7
|
balance
|
|
Cr20Ni80
|
0.08
|
0.02
|
0.015
|
0.6
|
0.75-1.6
|
20-23
|
balance
|
<0.5
|
≤1.0
|
|
Cr15Ni60
|
0.08
|
0.02
|
0.015
|
0.6
|
0.75-1.6
|
15-18
|
55-61
|
<0.5
|
balance
|
|
Cr20Ni35
|
0.08
|
0.02
|
0.015
|
1.0
|
1-3
|
18-21
|
34-37
|
-
|
balance
|
|
Cr20Ni30
|
0.08
|
0.02
|
0.015
|
1.0
|
1-3
|
18-21
|
30-34
|
-
|
balance
|