Shanghai Tankii Alloy Material Co.,Ltd
Shanghai Tankii Alloy Material Co.,Ltd First Quality, Sincere Service
Add to Cart
1.0*200 0Cr21Al6Nb FeCrAl heating resistance strip ribbon in stock for heating elements
1. Description
With the characteristics of high resistance, low coefficient of electric resistance, High operating temperature, good corrosion resistance under high temperature, It is widely used in industrial electric furnace, household electrical appliance and Far infrared ray device.
2. Specification
Wire:
Diameter: 0.15mm-8.0mm
Strip:
Thickness: 0.6mm-1.5mm
Width: over 40mm
3. Usage
It is mainly used in electric locomotive, diesel locomotive, metro vehicle and high speed moving car etc brake system brake resistor, electric ceramic cooktop, industrial furnace.
4. Features
Stable performance; Anti-oxidation; Corrosion resistance; High temperature stability; Excellent coil-forming ability; Uniform and beautiful surface condition without spots.
5. Packing detail
1) Coil (plastic spool) + compressed ply-wooden case + pallet
2) Coil (plastic spool) + carton + pallet
6. Products and services
1). Pass: ISO9001 certification, and SO14001cetification;
2). Fine after-sale services;
3). Small order accepted;
4). Stable properties in high temperature;
5). Fast delivery;
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | Other | ||
| Max | |||||||||||
| 0.05 | 0.025 | 0.025 | 0.70 | Max 0.6 | 21.0~23.0 | Max 0.60 | 5.0~7.0 | Bal. | Nb 0.5 | ||
| Max Continuous Service Temp | 1350ºC |
| Resistivity at 20ºC | 1.45 ohm mm2/m |
| Density | 7.1 g/cm3 |
| Thermal Conductivity | 46.1 KJ/m·h·ºC |
| Coefficient of Thermal Expansion | 16.0×10-6/ºC |
| Melting Point | 1510ºC |
| Tensile Strength | 637~784 Mpa |
| Elongation | Min 12% |
| Section Variation Shrink Rate | 65~75% |
| Repeatedly Bend Frequency | Min 5 times |
| Continuous Service Time | - |
| Hardness | 200-260HB |
| Micrographic Structure | Ferrite |
| Magnetic Property | Magnetic |
| 20ºC | 100ºC | 200ºC | 300ºC | 400ºC | 500ºC | 600ºC | 700ºC | 800ºC | 900ºC | 1000ºC | 1100ºC | 1200ºC |
| 1 | 0.997 | 0.996 | 0.994 | 0.991 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 |
Standard Specification:
| Grade | Main chemical composition | Hightest temperature ℃ |
Rrsistivity |
Melting point ℃ | Tensile strength N/mm² |
Elogation |
Working life |
Magnetic |
|||
| Cr | Al | Ni | Fe | ||||||||
| OCr21Al4 | 17-21 | 3-4 | - | - | 1100 | 1.23±0.06 | 1500 | 750 | ≥12 | ≥80/1250 | magnetic |
| OCr25Al5 | 23-26 | 4.5-6.5 | - | - | 1250 | 1.42±0.07 | 1500 | 750 | ≥12 | ≥80/1300 | magnetic |
| OCr21Al6Nb | 21-23 | 5-7 | - | - | 1350 | 1.43±0.07 | 1510 | 750 | ≥12 | ≥50/1350 | magnetic |
| OCr27Al7Mo2 | 22-24 | 5-7 | - | - | 1400 | 1.53±0.07 | 1520 | 750 | ≥10 | ≥50/1350 | magnetic |
| KSC | 26.8-27.8 | 6-7 | - | - | 1350 | 1.44±0.05 | 1510 | 750 | ≥16 | ≥60/1350 | magnetic |
| Cr20Ni80 | 20-23 | - | Rest | ≤1.0 | 1200 | 1.09±0.05 | 1400 | 750 | ≥20 | ≥80/1200 | Non-magnetic |
| Cr30Ni70 | 30 | - | Rest | ≤1.0 | 1250 | 1.18±0.05 | 1380 | 750 | ≥20 | ≥50/1250 | Non-magnetic |
| Cr15Ni60 | 15-18 | - | 55 | Rest | 1150 | 1.12±0.05 | 1390 | 750 | ≥20 | ≥80/1150 | Non-magnetic |
| Cr20Ni35 | 18-21 | - | 35 | Rest | 1100 | 1.04±0.05 | 1390 | 750 | ≥20 | ≥80/1100 | Weak magnetic |
| Cr20Ni30 | 20 | - | 32 | Rest | 1100 | 1.04±0.05 | 1390 | 750 | ≥20 | ≥80/1100 | Weak magnetic |