KD alloy Flat Bar/ Round Bars / Bolt 8mm 12mm Used As Furnaces Heating Lead-out Rod
Tankii DESCRIPTION OF FECRAL ALLOYS: KD alloys
FeCrAl alloys are characterized by excellent oxidation resistance and very good form stability resulting in long element life.
They are typically used in electrical heating elements in industrial furnaces and home appliances.
FeCrAl alloys have higher service temperature than NiCr Alloys and much lower prices. But they have lower stability and flexibility, easily to be fragile after a time circle
The grades of Electric furnace wire used for lead rod are various, according to the furnace temperature: stainless steel, 0Cr25Al5, 0Cr21Al6Nb, 0cr27Al7MO2 and other materials, our factory produces all variety of lead rod, with quality assurance!
Specifications: 10mm, 12mm, 14mm, 16mm, 18mm, 20mm, 25mm, 30mm, 35mm and so on.
It can be fine processing on the wire connecting rod, lead-out rod , such as Thread-cutting, slotting and so on.
TANKII FECRAL ALLOYS CHARACTERISTICS:
1) Manufactured according to international quality. System (ISO9001).
2) Stable resistance and long-life span.
3) Mill test certificate will be provided after production.
4) Size range wire:.0.018-10mm ribbons: 0.05-0.2*2-6mm strips: 0.05-5*5-250mm.
5) Good packing methods to keep goods no damage during delivery.
6) Customized lable, packing, OEM service..
7) 24 hours after-sale service.
KD alloy Flat Bar/ Round Bars / Bolt 8mm 12mm Used As Furnaces Heating Lead-out Rod
Application:
Heating elements for furnaces
Heating lead-out rod , connecting rod for furnaces.
MAIN CHARACTERISTICS OF TANKII FECRAL HEATING ALLOYS
Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
Nb0.5 | Mo1.8-2.2 | |||||||
Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
Density(g/cm3) | 7.40 | 7.10 | 7.16 | 7.25 | 7.35 | 7.10 | 7.10 | |
Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16.0 | 14.7 | 15.0 | 13.5 | 16.0 | 16.0 | |
Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
continuous servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | |
NiChrome bar or flat bar can also be used for bolt for furnaces.
KD alloy Flat Bar/ Round Bars / Bolt 8mm 12mm Used As Furnaces Heating Lead-out Rod
Photos:
Application:Heater lead-out rod:
KD alloy Flat Bar/ Round Bars / Bolt 8mm 12mm Used As Furnaces Heating Lead-out Rod
Please feel free to let me know if you have any inquiry on KD alloy bolt, bar, flat bar or rod.